Extruded Khoom Polyacetal Acetal Pom Sheet
Nqe lus piav qhia:
Yam khoom: | POM Sheet |
Xim: | dawb, dub |
Qhov ceev (g / cm3): | 1.4g / cm33 |
Muaj hom: | daim ntawv.rod |
Standard loj (mm): | 1000X2000MM, 620X1200MM |
Ntev (mm): | 1000 los yog 2000 |
Thickness (hli): | 1-200 hli |
Qauv | cov qauv dawb tuaj yeem muab rau kev kuaj xyuas zoo |
Chaw nres nkoj | Tian Jin, Suav teb |
Daim ntawv qhia lub cev:
Xim: | Dub | Khoov tensile stress / Tensile stress off shock: | 68/-Mpa | Critical Tracking Index (CTI): | 600 |
Loj: | 1.40 g / cm33 | Rhuav tensile hom: | 35% | Bonding peev: | + |
Thaum tshav kub kub tsis kam (nruam): | 115ºC | Tensile modulus ntawm elasticity: | 3100MPa | Sib cuag zaub mov: | + |
Thaum tshav kub kub tsis kam (lub sij hawm luv): | 140 | Compressive kev nyuaj siab ntawm ib txwm strain-1% / 2%: | 19/35MPa | Acid resistance: | + |
Melting point: | 165 ºC | Pendulum gap impact test: | 7 | Alkali tsis kam | + |
iav hloov kub: | _ | Kev sib txhuam coefficient: | 0.32 ib | Carbonated dej tsis kam: | + |
Linear thermal expansion coefficient (nruab nrab 23 ~ 100ºC): | 110 × 10-6 m / (mk) | Rockwell hardness: | M84 | Aromatic compound kuj: | + |
(nruab nrab 23-150ºC): | 125 × 10-6 m / (mk) | Dielectric zog: | 20 | Ketone tsis kam: | + |
Flammability (UI94): | HB | Volume resistance: | 1014Ω × cm | Thickness kam rau ua (mm): | 0 ~ 3% |
Kev nqus dej (dhau mus rau hauv dej ntawm 23ºC rau 24H): | 20% | Surface resistance: | 1013 Ω | ||
(Nyob rau hauv dej ntawm 23ºC: | 0.85% | Tus txheeb ze dielectric tsis tu ncua-100HZ / 1MHz: | 3.8 / 3.8 |
Daim ntawv thov:
Polyoxymethylene, feem ntau hu ua POM, nws yog cov thermoplastic engineering yas nrog cov ntsiab lus melting siab thiab siab.crystallinty, uas yog zoo heev rau machining ua hauj lwm ntawm lub tshuab dhos tsis siv neeg, tshwj xeeb tshaj yog rau precision tivthaiv manufacturing.